Magnetic Lubrication Technologies

Areas of application

• Grease lubrication of friction and rolling bearings in the high-temperature range
• Application, for example at tunnel kiln cars, baking, burn-in and drying furnaces, hot gas units, reaction vessels, boiler plants, roller and conveyor rollers in continuous furnaces, etc.
• Use at bearing points under influence of chemicals/fuel

Advantages and benefits

• Maximum water and steam resistance
• Extraordinary resistance to chemicals, for example to solvents, for example benzene, benzol, acetone, trichloroethylene and against inorganic acids, such as sulphuric acid, hydrochloric acid and nitric acid as well as stearic acids, alcohols and halogens
• Excellent plastic and elastomer compatibility
• For long-term lubrication of lubrication points subjected to high pressure up to 280°C
• Broad range of applications above the temperature limits of other lubricating greases
• Reduced maintenance and lubricant costs due to possible lifetime lubrication
• NSF H1 registered
• MOSH/MOAH-free (as per recipe)

Technical specifications

• lower operating temperature: -40 °C (< 1,400 hPa)
• upper operating temperature: 280 °C
• consistency: NLGI 2 NLGI grade (DIN ISO 2137)
• viscosity at (40°C): 390 mm²/s (base oil)
• four-ball test rig welding load: > 10,000 N

Applications

Thorough cleaning of the bearings from other lubricants, for example with OKS 2610/OKS 2611 universal cleaner is imperative. Subsequently blow out with dry air. Before filling for first time, remove anti-corrosion agent. Fill the bearing such that all functional surfaces are certain of being greased. Fill bearings running slowly completely, fill high-speed bearings (DN value > 150,000) only up to about 2/3 of the free space inside the bearing. The bearing and machine manufacturer's instructions should be observed. If old grease cannot be removed, restrict the quantity of grease so as to avoid overlubricating the bearing. Only mix with suitable lubricants.

Mounting paste for lubricating sliding points at which dark lubricants are not desired and where frictional corrosion is to be avoided.

Areas of application

• Lubrication of parts subject to high levels of stress such as plain, roller and rod-end bearings, spindles and guideways

Advantages and benefits

• Highly suitable for high-stressed lubrication points
• Highly effective caused by optimal combination of components
• Saving of maintenance and lubrication costs by reducing downtimes and corrective maintenance
• Reduction of down times due to wear

Technical specifications

• lower operating temperature: -30 °C (≤ 1,400 hPa)
• upper operating temperature: 120 °C (F50 (A/1500/6000), 100h)
• consistency: NLGI 2 NLGI grade (DIN ISO 2137)
• viscosity at (40°C): 100 mm²/s (base oil)
• four-ball test rig welding load: 3,600 N

Applications

For highest effectiveness, carefully clean the lubrication point, for example with OKS 2610 or OKS 2611 universal cleaner. Before filling for first time, remove anticorrosion agent. Fill bearing such that all functional surfaces are certain of being greased. Fill normal bearings up to about 1/3 of the free space inside the bearing. Low-speed bearings (DN value below 50 000) and their housings should be filled completely. The bearing and machine manufacturer´s instructions should be observed. Subsequent lubrication at the lubrication nipples by grease gun or by automatic lubrication system. Assess the lubrication frequency and quantity on basis of service conditions. If old grease cannot be removed, restrict the quantity of grease so as to avoid overlubricating the bearing. If lubrication frequencies tend to be low, you should aim for a full grease change. Only mix with suitable lubricants.

Areas of application

• Grease lubrication of plain and roller bearings with low bearing play as well as bearings with low coasting moments
• Lubrication for fast-running roller bearings
• Sealing lubrication of mating surfaces, for example ground-in parts such as taper plugs, dosing plungers and valves
• Maintenance lubrication of plastic and rubber parts with embrittlement protection and good frictional characteristics, particularly on metal surfaces

Advantages and benefits

• Temperature range from -60°C to 120°C
• Resistant to all alkali and acid cleaning agents and disinfectants
• Good wear protection through PTFE
• NSF H2 registration

Technical specifications

• lower operating temperature: -60 °C (≤ 1,400 hPa)
• upper operating temperature: 120 °C (F50 (A/1500/6000), 100h)
• consistency: NLGI 2 NLGI grade (DIN ISO 2137)
• viscosity at (40°C): approx. 30 mm²/s (base oil)
• four-ball test rig welding load: 2,000 N

Applications

Clean the lubricating points well for optimal effect. Before filling for first time, remove anti-corrosion agent. Fill the bearing such that all functional surfaces are certain of being greased. Fill normal bearings up to about 1/3 of the free space inside the bearing, high-speed bearings (DN value < 400,000) up to about 1/4. Low-speed bearings (DN value > 50,000) and their housings should be filled completely. In as far as available, the bearing and machine manufacturer's instructions should be observed. Subsequent lubrication at the lubrication nipples by grease gun or by automatic lubrication system. Assess the lubrication frequency and quantity on the basis of the service conditions. If old grease cannot be removed, restrict the quantity of grease so as to avoid over-lubricating the bearing. If lubrication frequencies tend to be low, you should aim for a full grease change. Caution: Only mix with suitable lubricants.

Areas of application

• Sealant and lubricant for cold and hot-water valves in vehicle heating systems or cooling circuits and for ground seals on glass taps and desiccators
• Lubrication of O-rings and rubber seals for assembly and during operation
• Lubrication of plastic parts

Advantages and benefits

• NSF H1 registered
• Tasteless and odourless
• Highly effective due to excellent adhesion on all materials
• Neutral behaviour with regard to plastics and elastomers
• Completely EPDM-compatible
• High long-term stability without drying out, hardening or bleeding
• Resistant to cold and hot water, as well as acetone, ethanol, ethylene glycol, glycerine and methanol
• MOSH/MOAH-free (as per recipe)

Technical specifications

• lower operating temperature: -40 °C
• upper operating temperature: 200 °C
• consistency: NLGI 3 NLGI grade (DIN ISO 2137)
• viscosity at (40°C): 9,500 mm²/s (base oil)

Applications

Clean the lubricating points well for optimal effect. Apply the grease evenly and thinly to the functional surfaces with a brush, spatula, etc. Avoid excesses. In as far as available, observe the machine manufacturer's instructions. Assess the lubrication frequency and quantity on basis of service conditions. Only mix with suitable lubricants. Caution: Plastic based on silicone, such as silicone rubber can be attacked by silicone grease. Silicone grease may not be used at sliding points under pure oxygen influence.

Synthetic High-Temperature Grease for the lubrication of bearings and sliding parts exposed to high temperatureand heavy loads but operating in slow to moderate speeds.

High-Temperature Grease, for Food Processing Technology
OKS 479 is a fully synthetic grease for food processing technology that is used to lubricate rolling and friction bearings as well as other machine elements under increased operating temperatures.

Oks 476 Food Grade Grease is a high-performance lubricant designed specifically for use in food processing and handling environments. This 1kg container of grease meets stringent safety and quality standards, ensuring it is safe for incidental contact with food. Its exceptional resistance to water and high temperatures makes it ideal for various applications, including machinery and equipment in food production facilities. The grease provides long-lasting protection against wear and corrosion, enhancing the efficiency and longevity of your equipment while maintaining compliance with food safety regulations.

Technical specifications

• lower operating temperature: -10 °C (≤ 1,400 hPa)
• upper operating temperature: 160 °C
• consistency: 1-2 NLGI grade (DIN ISO 2137)
• viscosity (at 40°C): 490 mm²/s (base oil)
• UFI: 35P3-G0PG-7001-U0QA

High-temperature screw paste on copper basis for preventing corrosion, seizing and binding.
Assembling screw threaded connections subjected to hightemperatures and corrosive influencesScrewed connections at pipe fittings, flange joints and fittingsin superheated steam linesCombustion chamber screwed connections and mountingbolts of gas and oil burnersScrewed connections at combustion engines, exhaustsystems, silencers and exhaust gas pipe connections